| FILAMENT
WOUND EPOXY/E-GLASS
#CT9/9505-20
| #CT9/9505-45 | #CT9/9505-55
#CT9/9505-20
(MADE FOR BENDING AND TENSION APPLICATIONS) |
| DENSITY |
0.072
lb./in.3 |
| HEAT
DISTORTION TEMPERATURE |
135°C |
| WATER
ABSORPTION (24 HRS.) |
0.01% |
| TENSLE
STRENGTH (LONGITUDINAL) |
110,000
psi |
| COMPRESSIVE
STRENGTH (LONGITUDINAL) |
50,000
psi |
| COMPRESSIVE
STRENGTH (CIRCUMFERENTIAL) |
26,000
psi |
| FLEXUAL
MODULUS (LONGITUDINAL) |
5.0
x 106 psi |
| FLEXUAL
MODULUS (CIRCUMFERENTIAL) |
1.1
x 106 psi |
| COEF.
OF THERMAL EXPANSION (LONG.) |
8.6
x 10-6in/in/°F |
| COEF.
OF THERMAL EXPANSION (CIRC.) |
4.8
x 10-6in/in/°F |
| DIELECTRIC
STRENGH |
400
V/mil |
^top
#CT9/9505-45
(MADE FOR TORQUE APPLICATIONS) |
| DENSITY |
0.072
lb./in.3 |
| HEAT
DISTORTION TEMPERATURE |
135°C |
| WATER
ABSORPTION (24 HRS.) |
0.01% |
| TENSLE
STRENGTH (LONGITUDINAL) |
22,000
psi |
| TENSLE
STRENGTH (CIRCUMFERENTIAL) |
22,000
psi |
| COMPRESSIVE
STRENGTH (LONGITUDINAL) |
26,000
psi |
| COMPRESSIVE
STRENGTH (CIRCUMFERENTIAL) |
26,000
psi |
| FLEXUAL
MODULUS (LONGITUDINAL) |
2.7
x 106 psi |
| FLEXUAL
MODULUS (CIRCUMFERENTIAL) |
2.7
x 106 psi |
| COEF.
OF THERMAL EXPANSION (LONG.) |
6.3
x 10-6in/in/°F |
| COEF.
OF THERMAL EXPANSION (CIRC.) |
6.3
x 10-6in/in/°F |
| DIELECTRIC
STRENGH |
400
V/mil |
^top
#CT9/9505-55
(MADE FOR INTERNAL PRESSURE APPLICATIONS) |
| DENSITY |
0.072
lb./in.3 |
| HEAT
DISTORTION TEMPERATURE |
135°C |
| WATER
ABSORPTION (24 HRS.) |
0.01% |
| TENSLE
STRENGTH (LONGITUDINAL) |
16,000
psi |
| TENSLE
STRENGTH (CIRCUMFERENTIAL) |
40,000
psi |
| COMPRESSIVE
STRENGTH (LONGITUDINAL) |
27,000
psi |
| COMPRESSIVE
STRENGTH (CIRCUMFERENTIAL) |
37,000
psi |
| FLEXUAL
MODULUS (LONGITUDINAL) |
1.3
x 106 psi |
| FLEXUAL
MODULUS (CIRCUMFERENTIAL) |
3.6
x 106 psi |
| COEF.
OF THERMAL EXPANSION (LONG.) |
4.5
x 10-6in/in/°F |
| COEF.
OF THERMAL EXPANSION (CIRC.) |
8.7
x 10-6in/in/°F |
| DIELECTRIC
STRENGH |
400
V/mil |
^top |